Used for pipeline coating, marine equipment, reinforced valves, steel structure building primer, electronic instrumentation, electrical insulation copper and aluminum wires, mechanical parts, pump bodies, chemical equipment, metal and non-metallic surfaces that are susceptible to chemical attack in wet environments Wait.

Standard and low temperature curing powder coating products are available.

High gloss (above 86%), glossy (76-85%), semi-gloss (50-75%), matt (20-50%) and matt (below 20%) products are available. The gloss can also be controlled according to the user's requirements.

Construction method:Construction by high-voltage electrostatic spraying or friction spraying

gun distance：About 150-300mm

preprocessing：Degrease, rust or phosphatize the workpiece by mechanical methods (manual grinding or sandblasting, etc.) and chemical methods, and then dry or dry naturally after rinsing with water.

curing conditions： 

Type A 200°C (workpiece temperature) 15 minutes (flat or matt)

Type B 180°C (workpiece temperature) 15 minutes (high light or matt)

Type C 140°C (workpiece temperature) 15 minutes (high light)

specific gravity：1.2-1.7（Varies by color and gloss）

Particle size distribution：100% less than 125 microns (can be adjusted according to the special requirements of coating)

fluidity：22-35nm

Utilization：8-12 square meters/kg, film thickness 60 microns (calculated at 100% powder coating usage rate)

transportation：Non-dangerous goods, suitable for various transportation methods, avoid prolonged direct sunlight, and avoid water, oil and other chemical contamination.

Store in a ventilated, dry and clean room below 25°C, keep away from fire, heating, avoid direct sunlight, and strictly prohibit open-air stacking. The powder is stable in storage for 12 months under these conditions. If the storage period is exceeded, re-inspection can be carried out. If the result meets the requirements, it can still be used.